Polyester films have excellent dimensional stability, high tensile, tear, and impact strengths, and ultimate elongation up to 120% of its original dimensions. These films exhibit low water absorption and good resistance to oils, greases, strong acids, and organic solvents. They also retain electrical properties, dielectric strength and dielectric constant in continuous operating temperatures from -100°F to 350°F (-73°C to 177°C).
Applications include transformer and capacitor wrapping, printed circuit board fabrication, splicing tapes, composite bonding protection, and low-cost masking.
Part # Color Adhesive
SystemBacking
ThicknessAdhesive
ThicknessTotal
ThicknessAdhesion Strength Tensile Strength Elong. Temperature Range mil mm mil mm mil mm oz/in g/cm lbs/in kg/cm % Min °F Max °F Min °C Max °C FILM-Polyester MCL050 Clear proprietary 1 0.025 1.0 0.038 2.0 0.050 3 28 25 4.5 100 -100 400 -73 200 MCL075 Clear proprietary 2 0.050 1.0 0.038 3.0 0.075 3 28 50 8.9 120 -100 400 -73 200 MCL150 Clear proprietary 5 0.125 1.0 0.038 6.0 0.150 3 28 100 17.9 100 -100 400 -73 200 M50 White S 1.0 0.025 1.5 0.038 2.5 0.064 25 276 25 4.5 100 -100 350 -73 177 M52 Clear S 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -100 350 -73 177 M717 Red S 1.0 0.025 2.8 0.071 3.8 0.097 30 331 25 4.5 100 -100 350 -73 177 M741 Blue S 1.0 0.025 2.0 0.051 3.0 0.076 25 276 25 4.5 100 -100 350 -73 177 M746 Red/Bl S 1.0 0.025 0.8 0.020 1.8 0.046 13 143 25 4.5 100 -100 350 -73 177 M751 Yellow S 1.0 0.025 2.0 0.051 3.0 0.076 25 276 25 4.5 100 -100 350 -73 177 M758 Black S 1.0 0.025 1.5 0.038 2.5 0.064 25 276 25 4.5 100 -100 350 -73 177 M803 Blue S 1.0 0.025 2.0 0.051 3.0 0.076 25 276 25 4.5 100 -100 350 -73 177 M815 Clear S 1.0 0.025 2.0 0.051 3.0 0.076 30 331 25 4.5 100 -100 350 -73 177 M823 Blue S 1.0 0.025 1.8 0.046 2.8 0.071 30 331 25 4.5 100 -100 350 -73 177 M824 Blue S 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -100 350 -73 177 M66/
M730Green S 1.5 0.038 1.0 0.025 2.5 0.064 25 276 35 6.3 100 -100 350 -73 177 M887 Emerald S 2.0 0.051 1.5 0.038 3.5 0.089 40 441 50 8.9 120 -60 350 -51 177 M56 Clear R 1.0 0.025 1.5 0.038 2.5 0.064 45 496 25 4.5 100 0 325 -18 163 M64 Yellow R 1.0 0.025 1.5 0.038 2.5 0.064 50 551 25 4.5 100 0 325 -18 163 M734 Orange R 1.0 0.025 0.6 0.015 1.6 0.041 6 66 25 4.5 100 0 325 -18 163 M788 Aqua R 1.0 0.025 0.5 0.013 1.5 0.038 5 55 25 4.5 100 0 325 -18 163 M797 Mustard R 1.0 0.025 2.0 0.051 3.0 0.076 30 331 25 4.5 100 0 325 -18 163 M851 Green R 1.0 0.025 2.0 0.051 3.0 0.076 15 165 25 4.5 100 0 350 -18 177 M783 Pink R 2.0 0.051 1.7 0.043 3.7 0.094 35 386 50 8.9 120 0 325 -18 163 M852 Green R 2.0 0.051 2.0 0.051 4.0 0.102 15 165 50 8.9 120 0 350 -18 177 M855 Green R 5.0 0.127 2.0 0.051 7.0 0.178 6 66 100 17.9 100 0 350 -18 177 M69 Clear A/A 1.0 0.025 3.0 0.076 4.0 0.102 30 331 25 4.5 100 -20 325 -29 163 M37-
1HYLYellow A 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -20 325 -29 163 M60 Clear A 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -20 325 -29 163 M705 Black A 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -20 325 -29 163 CW01 Natural A 5 0.127 2 0.051 7 0.178 50 558 275 4.9 20 -4 311 -20 155 Film-Polyester +
Polyester films have excellent dimensional stability, high tensile, tear, and impact strengths, and ultimate elongation up to 120% of its original dimensions. These films exhibit low water absorption and good resistance to oils, greases, strong acids, and organic solvents. They also retain electrical properties, dielectric strength and dielectric constant in continuous operating temperatures from -100°F to 350°F (-73°C to 177°C).
Applications include transformer and capacitor wrapping, printed circuit board fabrication, splicing tapes, composite bonding protection, and low-cost masking.
CHR® Polyester Film Tape -- Products
Part # Color Adhesive
SystemBacking
ThicknessAdhesive
ThicknessTotal
ThicknessAdhesion Strength Tensile Strength Elong. Temperature Range mil mm mil mm mil mm oz/in g/cm lbs/in kg/cm % Min °F Max °F Min °C Max °C FILM-Polyester MCL050 Clear proprietary 1 0.025 1.0 0.038 2.0 0.050 3 28 25 4.5 100 -100 400 -73 200 MCL075 Clear proprietary 2 0.050 1.0 0.038 3.0 0.075 3 28 50 8.9 120 -100 400 -73 200 MCL150 Clear proprietary 5 0.125 1.0 0.038 6.0 0.150 3 28 100 17.9 100 -100 400 -73 200 M50 White S 1.0 0.025 1.5 0.038 2.5 0.064 25 276 25 4.5 100 -100 350 -73 177 M52 Clear S 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -100 350 -73 177 M717 Red S 1.0 0.025 2.8 0.071 3.8 0.097 30 331 25 4.5 100 -100 350 -73 177 M741 Blue S 1.0 0.025 2.0 0.051 3.0 0.076 25 276 25 4.5 100 -100 350 -73 177 M746 Red/Bl S 1.0 0.025 0.8 0.020 1.8 0.046 13 143 25 4.5 100 -100 350 -73 177 M751 Yellow S 1.0 0.025 2.0 0.051 3.0 0.076 25 276 25 4.5 100 -100 350 -73 177 M758 Black S 1.0 0.025 1.5 0.038 2.5 0.064 25 276 25 4.5 100 -100 350 -73 177 M803 Blue S 1.0 0.025 2.0 0.051 3.0 0.076 25 276 25 4.5 100 -100 350 -73 177 M815 Clear S 1.0 0.025 2.0 0.051 3.0 0.076 30 331 25 4.5 100 -100 350 -73 177 M823 Blue S 1.0 0.025 1.8 0.046 2.8 0.071 30 331 25 4.5 100 -100 350 -73 177 M824 Blue S 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -100 350 -73 177 M66/
M730Green S 1.5 0.038 1.0 0.025 2.5 0.064 25 276 35 6.3 100 -100 350 -73 177 M887 Emerald S 2.0 0.051 1.5 0.038 3.5 0.089 40 441 50 8.9 120 -60 350 -51 177 M56 Clear R 1.0 0.025 1.5 0.038 2.5 0.064 45 496 25 4.5 100 0 325 -18 163 M64 Yellow R 1.0 0.025 1.5 0.038 2.5 0.064 50 551 25 4.5 100 0 325 -18 163 M734 Orange R 1.0 0.025 0.6 0.015 1.6 0.041 6 66 25 4.5 100 0 325 -18 163 M788 Aqua R 1.0 0.025 0.5 0.013 1.5 0.038 5 55 25 4.5 100 0 325 -18 163 M797 Mustard R 1.0 0.025 2.0 0.051 3.0 0.076 30 331 25 4.5 100 0 325 -18 163 M851 Green R 1.0 0.025 2.0 0.051 3.0 0.076 15 165 25 4.5 100 0 350 -18 177 M783 Pink R 2.0 0.051 1.7 0.043 3.7 0.094 35 386 50 8.9 120 0 325 -18 163 M852 Green R 2.0 0.051 2.0 0.051 4.0 0.102 15 165 50 8.9 120 0 350 -18 177 M855 Green R 5.0 0.127 2.0 0.051 7.0 0.178 6 66 100 17.9 100 0 350 -18 177 M69 Clear A/A 1.0 0.025 3.0 0.076 4.0 0.102 30 331 25 4.5 100 -20 325 -29 163 M37-
1HYLYellow A 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -20 325 -29 163 M60 Clear A 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -20 325 -29 163 M705 Black A 1.0 0.025 1.5 0.038 2.5 0.064 30 331 25 4.5 100 -20 325 -29 163 CW01 Natural A 5 0.127 2 0.051 7 0.178 50 558 275 4.9 20 -4 311 -20 155 Film-Polyimide +
Polyimide films are employed because of their extreme heat resistance. Service temperatures range from
-100°F to +500°F (-73°C to +260°C). These flame retardant films exhibit high tensile strength and conformability, good solvent resistance, excellent dielectric strength and good abrasion resistance.
Polyimide tape applications include electrical insulation, capacitor, transformer, and coil wrapping, electronic assembly, and wave solder protection.
CHR® Brand Polyimide Film Tape Products
Part # Color Adhes.
Sys.Backing
ThicknessAdhesive
ThicknessTotal
ThicknessAdhesion
StrengthTensile
StrengthElong. Temperature Range mil mm mil mm mil mm oz/in g/cm lbs/in kg/cm % Min
°FMax
°FMin
°CMax
°CFILM-Polyimide KCL050 Amb proprietary 1 0.025 1.0 0.025 2.0 0.05 28 30 5.4 50 -100 600 -73 315 2345-1 Amb S 1.0 0.025 1.5 0.038 2.5 0.064 25 276 30 5.4 50 -100 500 -73 260 2345-2 Amb S 2.0 0.051 1.5 0.038 3.5 0.089 25 276 50 8.9 75 -100 500 -73 260 2345-5 Amb S 5.0 0.127 1.5 0.038 6.5 0.165 20 221 150 26.8 75 -100 500 -73 260 K104 Amb S 0.5 0.013 1.0 0.025 1.5 0.038 15 165 10 1.8 25 -100 500 -73 260 K201 Amb S 1.0 0.025 1.5 0.038 2.5 0.064 25 276 30 5.4 50 -100 500 -73 260 K202 Amb S 2.0 0.051 1.5 0.038 3.5 0.089 25 276 50 8.9 75 -100 500 -73 260 K250 Amb S 1.0 0.025 1.5 0.038 2.5 0.064 30 220 30 5.4 50 -100 500 -73 260 K350 Amb S 2.0 0.051 1.5 0.038 3.5 0.089 20 220 50 8.9 75 -100 500 -73 260 K102 Amb A 1.0 0.025 1.5 0.038 2.5 0.064 30 331 30 5.4 50 -20 350 -29 177 K109 Amb A 2.0 0.051 1.5 0.038 3.5 0.089 30 331 50 8.9 75 -20 350 -29 177 K290-
ESDAmb S 1.0 0.025 1.5 0.038 2.5 0.064 20 220 30 5.4 50 -100 500 -73 260 K100 Amb S/S 1.0 0.025 3.5 0.089 4.5 0.114 20 220 30 5.4 50 -100 500 -73 260 Film-PTFE +
PTFE films provide a conformable release surface and exhibit a remarkably low coefficient of friction and non-stick properties. PTFE films have high temperature resistance and are virtually unaffected by all chemicals. At elevated temperatures, PTFE film still retains excellent tensile strength. Service temperatures range from -100°F to +500°F (-73°F to +260°C).
Film applications include high temperature coil and capacitor wrapping, composite bonding, masking, and conveyor release linings.
CHR® Brand PTFE Film Tape Products
Part # Color Adhes.
Sys.Backing
ThicknessAdhesive
ThicknessTotal
ThicknessAdhesion
StrengthTensile
StrengthElong. Temperature Range mil mm mil mm mil mm oz/in g/cm lbs/in kg/cm % Min
°FMax
°FMin
°CMax
°CFILM-PTFE Skived 2045-2 Gray S 2.0 0.051 1.5 0.038 3.5 0.089 30 331 15 2.7 325 -100 500 -73 260 2045-3 Gray S 3.0 0.076 1.5 0.038 4.5 0.114 35 386 20 3.6 350 -100 500 -73 260 2045-5 Gray S 5.0 0.127 1.5 0.038 6.5 0.165 40 441 30 5.4 400 -100 500 -73 260 2045-10 Gray S 10.0 0.250 1.5 0.038 11.5 0.292 50 551 55 10.7 450 -100 500 -73 260 2042-2 Gray A 2.0 0.051 1.5 0.038 3.5 0.089 25 276 15 2.7 300 -100 350 -73 177 2042-3 Gray A 3.0 0.076 1.5 0.038 4.5 0.114 30 331 20 3.6 375 -100 350 -73 177 2042-5 Gray A 5.0 0.127 1.5 0.038 6.5 0.165 35 386 30 5.4 400 -100 350 -73 177 2042-10 Gray A 10.0 0.250 1.5 0.038 11.5 0.292 55 606 55 9.9 450 -100 350 -73 177 TV350 Wh S 2.0 0.051 1.5 0.038 3.5 0.089 25 276 15 2.7 250 -100 500 -73 260 T Wh S 3.0 0.076 3.0 0.076 6.0 0.152 30 331 20 3.6 275 -100 500 -73 260 TV Wh S 5.0 0.127 1.5 0.038 6.5 0.165 35 386 30 5.4 275 -100 500 -73 260 TH Wh S 10.0 0.250 2.5 0.063 12.5 0.318 55 606 60 10.8 300 -100 500 -73 260 High-Modulus 2250-2 Gray R 2.0 0.051 1.5 0.038 3.5 0.089 25 276 30 5.4 150 -80 325 -40 163 2253-2 Gray A 2.0 0.051 1.5 0.038 3.5 0.089 30 331 30 5.4 150 -40 350 -40 177 2254-2 Gray S 2.0 0.051 1.5 0.038 3.5 0.089 35 386 30 5.4 150 -40 500 -40 260 2255-2 Gray S 2.0 0.051 1.5 0.038 3.5 0.089 30 331 30 5.4 150 -100 500 -73 260 2255-3 Gray S 3.0 0.076 1.5 0.038 4.5 0.114 35 386 45 8.0 175 -100 500 -73 260 2255-5 Gray S 5.0 0.125 1.5 0.038 6.5 0.165 40 441 60 10.7 175 -100 500 -73 260 2255-6 Gray S 6.0 0.152 1.5 0.038 7.5 0.191 45 496 65 11.7 200 -100 500 -73 260 NOTE: 2255 product series also available with silicone adhesive in 4, 6, 7 and 10 mil backing thickness HM350 Wh S 2.0 0.051 1.5 0.038 3.5 0.089 25 276 25 4.5 150 -100 500 -73 260 HM426 Gray S 2.0 0.064 1.5 0.038 3.5 0.089 25 276 25 4.5 150 -100 500 -73 260 HM430 Wh A 2.0 0.064 1.5 0.038 3.5 0.089 25 276 25 4.5 150 -20 350 -29 177 HM650 Wh S 5.0 0.127 1.5 0.038 6.5 0.165 30 331 45 8.0 200 -100 500 -73 260 Enhanced High Modulus R233 Gray A 5.0 0.125 1.5 0.038 6.5 0.165 30 331 75 13.0 150 -40 350 -40 177 R253 Gray S 5.0 0.125 1.5 0.038 6.5 0.165 40 441 75 13.0 110 -100 500 -73 260 Extruded 2265-2 Clear S 2.0 0.051 1.5 0.038 3.5 0.089 35 386 25 4.5 200 -100 500 -73 260 2265-5 Clear S 5.0 0.127 2.0 0.051 7.0 0.178 45 496 65 11.8 250 -100 500 -73 260 2275-2 Rust S 2.3 0.058 1.9 0.048 4.2 0.107 40 441 45 8.0 110 -100 500 -73 260 2283-2 Rust A 2.0 0.051 2.0 0.051 4.0 0.102 30 331 30 5.0 150 -40 350 -40 177 2285-2 Rust S 2.0 0.051 1.5 0.038 3.5 0.089 30 331 30 5.0 175 -100 500 -73 260 2285-5 Rust S 5.0 0.127 1.5 0.038 6.5 0.165 40 441 75 13.0 200 -100 500 -73 260 Film-Rulon® +
Rulon® films offer superior abrasion resistance when compared to conventional PTFE films. Service temperatures range from -100°F to 500°F (-73°C to +260°C). In rotating bearing tests, it provided a 500-fold increase in wear resistance over standard PTFE.
Applications include bearing liners, chute and guide rail coverings.
Saint-Gobain CHR® Rulon® tapes combines a low coefficient of friction with the high temperature stability of PTFE. Rulon also offers outstanding abrasion resistance, which equates to a 500-fold increase in wear resistance over PTFE in rotating bearing tests. Rulon backing is chemically inert and offers excellent high temperature resistance. RU’s tape construction is stable, non-toxic and weather resistant. The film surface is self-lubricating and the backing is conformable. RU tape is supplied with a peel off release liner. With silicone adhesive Saint-Gobain CHR® Rulon tape will survive temperatures up to 280°C.
- Static Coefficient of Friction = 0.05 - 0.1
- Dynamic Coefficient of Friction = .12 - .15
Properties Units (metric) Values (metric) CHR® RULON® TAPES Specific gravity n/a 2.22 Hardness Shore D 60 - 75 Water absorption % 0 Tensile strength psi (MPa) 2,000 (13.8) Elongation % 175 Deformation under load 1,500 psi, 24 hr, RT % 5.0 Izod impact strength ft/lb/in (J/m) 6.0 (320) Thermal conductivity BTU•in/hr•Ft2•F°) (W/m•K) 2.3 (0.33) Operating temperature range °F (°C) -400 to 550 (-240 to 288) Flammability in/min (m/s) non-flammable Maximum pressure (P) psi (MPa) 1,000 (6.9) Maximum velocity with no pressure (V) ft/min (m/s) 400 (2) Maximum PV psi•ft/min (MPa•m/s) 10,000 (0.35) Minimum mating surface hardness RC 35 Film-UHMW +
UHMW polyolefin film tape provides anti-sticking and abrasion resistance properties for application temperatures ranging from -100°F to 225°F (-73°C to +107°C).
Applications include bearings, chute and guide rail coverings.
CHR® Brand UHMW Film Tape Products
Part # Color Adhes.
Sys.Backing
ThicknessAdhesive
ThicknessTotal
ThicknessAdhesion
StrengthTensile
StrengthElong. Temperature Range mil mm mil mm mil mm oz/in g/cm lbs/in kg/cm % Min °F Max °F Min °C Max °C FILM-UHMW 2300-5R Nat R 5.0 0.127 2.0 0.051 7.0 0.178 55 606 40 7.0 350 0 225 -18 107 2300-10R Nat R 10.0 0.250 2.0 0.051 12.0 0.305 55 606 80 14.5 400 0 225 -18 107 2302-3R Nat A 3.0 0.076 1.5 0.038 4.5 0.114 35 386 20 3.6 300 -40 225 -40 107 2302-5R Nat A 5.0 0.127 1.5 0.038 6.5 0.165 45 496 40 7.0 350 -40 225 -40 107 2302-10R Nat A 10.0 0.250 1.5 0.038 11.5 0.292 50 551 80 14.5 425 -40 225 -40 107 2302-20R Nat A 20.0 0.500 1.5 0.038 21.5 0.546 50 551 145 26.3 500 -40 225 -40 107 NOTE: For 23XX product series, a blue PE liner is standard.
CHR® FEP, Polyester, Polyimide, PTFE, Rulon®, UMHW, and Fluoropolymer film backed tape
Saint-Gobain Performance Plastics offers a broad range of PSA tapes serving industrial and commercial users. Produced from a variety of film, fabric, metal, laminations or paper substrates with acrylic, silicone, or natural rubber adhesive systems, Saint-Gobain is uniquely able to produce outstanding, and sometimes proprietary products.
Our combined expertise in fabrics, films, silicones and coatings gives you confidence in our team approach to providing solutions to critical applications.
Quick Links
Certifications
Terms & Conditions
- Procurement
- Sales
CRI Rugged
Your sourcing specialist
Since 1983
SERVICE
Make us your one stop shop for electronic
components and value-added services
DISTRIBUTION
RSI is a global distributor, supplying local industries and global markets
LAND BASED DRILLING
RSI supplying to local industries
and global markets
GLOBAL DISTRIBUTOR
RSI, building creditability & trust for
30+ years!
QUALITY
RSI is a global distributor, supplying local industries and global markets
MASS TRANSIT
ELECTRO-MECHANICAL
DISTRIBUTION
since 1983
NIST
800-171
RSI, Inc.
An authorized distributor of electro-mechanical parts and services to global industries and markets such as; (DOD) Department of Defense, Energy Markets, Commercial Aerospace, Industrial Markets, and Transportation Industries. Contact Us
- Top Quality Products
- On-time Delivery
- Exceptional Service
- Competitive Pricing
- Value-add Services
- Identification Products
Overview
RSI, Inc.
Contact us
Inventory Search
WHO WE ARE
WHAT WE DO
LOCATIONS